Abstract :
Bioactive glass (BG), calcium hydroxyapatite (HA), and ZrO2 dopedHAthin filmswere grown by pulsed laser deposition on Ti substrates. AnUV
KrF* (l = 248 nm, t 7 ns) excimer laser was used for the multi-pulse irradiation of the targets. The substrates were kept at room temperature or
heated during the filmdeposition at values within the (400–550 8C) range. The depositions were performed in oxygen andwater vapor atmospheres, at
pressure values in the range (5–40 Pa). The HA coatings were heat post-treated for 6 h in a flux of hot water vapors at the same temperature as applied
during deposition. The surface morphology, chemical composition, and crystalline quality of the obtained thin filmswere studied by scanning electron
microscopy, atomic force microscopy, and X-ray diffractometry. The films were seeded for in vitro tests with Hek293 (human embryonic kidney) cells
that revealed a good adherence on the deposited layers. Biocompatibility tests showed that cell growth was better on HA than on BG thin films.