Microstructure and properties of duplex (Ti:N)-DLC/MAO coating on magnesium alloy

Ti and N co-doped diamond-like carbon ((Ti:N)-DLC) film was deposited on the MAO coated substrate using a hybrid beam deposition system, which consists of a DC magnetron sputtering of Ti target and a linear ion source (LIS) with C2H2 and N2 precursor gas. The microstructure and properties of the duplex (Ti:N)-DLC/MAO coating were investigated. Results indicate that the (Ti:N)-DLC top film with TiN crystalline phase was formed. Ti and N co-doping resulted in the increasing ID/IG ratio. The significant improvement in the wear and corrosion resistance of duplex (Ti:N)-DLC/MAO coating was mainly attributed to the increased binding strength, lubrication characteristics and chemical inertness of (Ti:N)-DLC top film. The superior low-friction and anti-corrosion properties of duplex (Ti:N)-DLC/MAO coating make it a good candidate as protective coating on magnesium alloy.