Effect of substrate temperature and deposition rate on the morphology and optical properties of Ti films

Titanium films are deposited on transparent fluorine-doped tin oxide (FTO) glass substrates by DC magnetron sputtering process. Influences imposed by sputtering rate and substrate temperature on surface morphology and optical properties of the deposited Ti films are investigated. We observed that all the sputtered films exhibit uniform and compact surface morphology without peeling and cracking. Morphology of the films is studied using atomic force microscopy (AFM) and X-ray diffraction (XRD). The optical properties of the films are investigated using UV–vis spectroscopy. The morphological studies indicate that by increasing the substrate temperature from room temperature to 250 °C and/or decreasing sputtering rate from 660 Å/min to 540 Å/min the surface roughness decreased from 73.4 to 31.0 nm and the grain size increases from 50.76 nm to 163.93 nm. An important effect of the root mean square (RMS) surface roughness and grain size is modification of the films optical properties. In fact, an enhancement of refractive index n for the Ti films deposited at high substrate temperature and/or high deposition rate is observed, that is attributed to reduction of RMS roughness. This effect is attributed to increment of fractional volume which leads to an increase in density of deposited film. Thus, by controlling the sputtering conditions one can reach to the desired morphological and optical properties.