Hydrogen adsorption on rhodium: Hydride formed on the surface of thin rhodium films

H2 interaction with thin Rh films deposited on Pyrex glass under UHV conditions has been studied by simultaneous measurement of work function changes ΔΦ and hydrogen pressure P, at selected constant temperatures: 78 and 298 K. Prior to the adsorption experiments the thin film topography was illustrated using the AFM and STM methods. The influence of hydrogen adsorption on the resistance of thin Rh film was examined in the course of an independent experiment. The number of sites accessible for adsorption on the thin Rh film surface was found determining population of oxygen adatoms within the monolayer at 78 K, when incorporation of these adspecies below the surface is negligible. It was established that at all examined temperatures hydrogen adsorption led to coverage Θ approaching 1 under equilibrium pressure below 10−3 Pa, increasing the work function. Under higher H2 pressure an additional uptake of hydrogen leading to Θ ∼ 1.68 at 298 K, and to Θ ∼ 2 at 78 K is reached. On this surface at low temperatures there exist weakly bound, reversibly adsorbed, positively charged adspecies characteristic for hydrogen adsorption on transition metal hydrides. The change of thin Rh film resistance caused by hydrogen adsorption was not measurable.