Preparation and antibacterial effect of plasma sprayed wollastonite coatings loading silver

In this work, the plasma sprayed wollastonite coating was soaked in 5 wt% AgNO3 solution at room temperature to load silver for improving its antibacterial effect. The surface characteristics of the silver-loaded coating were investigated by SEM, EDS and XRD. The release rate of silver from the coating was measured by ICP-OES in deionized water. The osteotoxicity of the silver-loaded coating was evaluated by in vitro cell culturing test. The antibacterial activity against Staphylococcus aureus was examined by Zone of Inhibition test. The results showed that the loaded silver reacted with the wollastonite coating to form silver silicate, which ensured a sustained release of silver in deionized water for as long as 50 days. The antibacterial activity and cell culturing tests confirmed that the silver released from silver-loaded wollastonite coating had strong inhibition against the growth of S. aureus, while they did not exhibit any adverse effects on the osteoblasts proliferation.