Electronic properties of the surface of perylene tetracarboxylic acid dianhydride film upon deposition of the ultrathin conjugated layers of Pyronine B

Ultrathin conjugated layers of Pyronine B were thermally deposited in UHV on the surface of perylene tetracarboxylic acid dianhydride (PTCDA) film. The structure of unoccupied electron states located 5–20 eV above the Fermi level (EF) and the surface potential were monitored during the Pyronine B overlayer deposition, using an incident beam of low-energy electrons according to the total current electron spectroscopy (TCS) method. Electronic work function of the PTCDA surface changed from 4.9 ± 0.1 eV, during the Pyronine B deposition due to the change of the contents of the surface layer, until it reached a stable value 4.6 ± 0.1 eV at the Pyronine B film thickness 8–10 nm. The interface dipole corresponds to electron transfer from the Pyronine B overlayer to the PTCDA surface and the polarization in the Pyronine B overlayer was found confined within approximately 1 nm near the interfaces. The edges of major bands of density of unoccupied electronic states (DOUS) of PTCDA substrate and of the Pyronine B overlayer were unaffected by the process of the interface formation. The major TCS spectral features of the Pyronine B film corresponding to the DOUS band edges were identified and the assignment of the π*, σ*(C–C) and σ*(Cdouble bond; length as m-dashC) character was suggested.