Facile synthesis and characterization of SnTe films

In this paper, we reported a novel, simple, and cost-effective route to SnTe films. The films were prepared by a chemical bath method, at room temperature and ambient pressure, using conventional chemicals as starting materials with or without surfactant. The films were characterized by X-ray diffraction, X-ray photoelectron spectroscopy and field-emission scanning electron microscopy, respectively. The SnTe film deposited without surfactant consists of nanoparticles (∼100 nm). The film deposited using polyethyleneglycol (PEG) as the surfactant consists of nanoparticles with size of ∼25 nm, whereas the film deposited using polyvinylpyrrolidone (PVP) as the surfactant consists of rough rod-like nanostructures (∼50 in diameter and ∼500 nm in length), besides nanoparticles (∼40–180 nm). The SnTe film deposited with PEG is smoother and denser. The formation mechanism of the SnTe films was proposed.