Synthesis and characterization of biodegradable poly(l-lactide)/layered double hydroxide nanocomposites

This study reports the preparation and physical properties of biodegradable nanocomposites fabricated using poly(l-lactide) (PLLA) and magnesium/aluminum layered double hydroxide (MgAl-LDH). The MgAl-LDH with molar ratio of Mg/Al = 2 were synthesized by the co-precipitation method. In order to improve the chemical compatibility between PLLA and LDH, the surface of LDH was organically-modified by polylactide with carboxyl end group (PLA–COOH) using ion-exchange process. Then, the PLLA/LDH nanocomposites were prepared by solution intercalation of PLLA into the galleries of PLA–COOH modified LDH (P-LDH) in tetrahydrofuran solution. Both X-ray diffraction data and Transmission electron microscopy images of PLLA/P-LDH nanocomposites indicate that the P-LDHs are randomly dispersed and exfoliated into the PLLA matrix. Mechanical properties of the fabricated 1.2 wt.% PLLA/P-LDH nanocomposites show significant enhancements in the storage modulus when compared to that of neat PLLA. Adding more P-LDH into PLLA matrix induced a decrease in the storage modulus of PLLA/P-LDH nanocomposites, probably due to the excessive content of PLA–COOH moleculars with low mechanical properties. The thermal stability and degradation activation energies of the PLLA and PLLA/P-LDH nanocomposites can also be discussed.