Effect of coupling agent and nanoclay on properties of HDPE, LDPE, PP, PVC blend and Phargamites karka nanocomposite

High density polyethylene (HDPE), low density polyethylene (LDPE), polypropylene (PP) and poly(vinyl chloride) (PVC) were solution blended by using a mixture of xylene and tetrahydrofuran as solvent and polyethylene-co-glycidyl methacrylate (PE-co-GMA) as compatibilizer. The minimum ratio of solvents to obtain a homogenous solution was optimised. Wood polymer composites (WPC) were prepared by using solution blended polymer, wood flour and nanoclay. X-ray diffraction studies of WPC treated with 1 and 3 phr nanoclay showed higher exfoliation compared to WPC treated with 5 phr nanoclay. TEM study also supported the above findings. FTIR studies indicated an interaction between wood, PE-co-GMA and clay. SEM study indicated an increase in miscibility among polymers due to addition of PE-co-GMA as compatibilizer. Thermal stability improved on addition of clay to the WPC. WPC treated with 3 phr clay showed highest mechanical properties. Hardness and water absorption were improved significantly with the addition of nanoclay to wood/polymer composite.