Ar+ ion milling-induced suppression of surface oxidation in Fe70Co30 thin films

We show from the depth-resolved X-ray absorption analysis that the degree of surface oxidation of Fe70Co30 thin films is reduced by Ar+ ion milling even if the film is exposed to air after ion milling. The milled film has thinner surface oxide layer and smaller ratio of Fe oxide component in the surface layer than those of the as-deposited film. It is also indicated that selective oxidation of Fe proceeds accompanied by the movement of Fe atoms toward the surface. The suppression of oxidation is explained by the obstruction of Fe movement toward the surface by the milling-induced disorder.