Characterization of CBD grown ZnO films with high c-axis orientation

Highly c-axis oriented ZnO films were deposited on seeded glass substrates. Successive ionic layer adsorption and reaction (SILAR) method and chemical bath deposition (CBD) method were used to obtain seed layers and ZnO films. To see the effects of seed layer and deposition time, structural (e.g. grain size, microstrain and dislocation density), morphological, and electrical (e.g. resistivity, activation energy) properties of the films were investigated by scanning electron microscopy, X-ray diffraction, and four point probe method. From the SEM images, resultant structures were found as well defined nanorods nearly perpendicular to the substrate surfaces and densely cover the substrates. The XRD patterns showed that ZnO films have hexagonal wurtzite structure with a preferred c-axis orientation along (002) plane. C-axis orientation was also supported by texture coefficient calculations. The lattice parameters of the structures were determined as a = 3.2268 Å, b = 5.2745 Å, α = β = 90° and γ = 120°. From the XRD patterns, it was revealed that, microstrain and dislocation density values of the structures decreased whereas grain size increased. This was attributed to enhancement occurred in lattice structure of the ZnO films. Activation energy values of the films were found in between 0.12 and 0.15 eV from the dark electrical resistivity-temperature characteristics in a temperature range of 300–500 K.