Structural characterization of phase transition of Al2O3 nanopowders obtained by polymeric precursor method

Nanocrystalline Al2O3powders have been synthesized by the polymeric precursor method. A study of the evolution of crystalline phases of obtained powders was accomplished through X-ray diffraction, micro-Raman spectroscopy and refinement of the structures through the Rietveld method. The results obtained allow the identification of three steps on the image-Al2O3 to image-Al2O3 phase transition. The single-phase image-Al2O3 powder was obtained after heat-treatment at 1050 image C for 2 h. A study of the morphology of the particles was accomplished through measures of crystallite size, specific surface area and transmission electronic microscopy. The particle size is closely related to image-Al2O3 to image-Al2O3 phase transition.