Surface strengthening using a self-protective diffusion paste and its application for ballistic protection of steel plates

This paper deals with surface strengthening of steel plates using a self-protective diffusion paste. During the surface strengthening process, a paste containing carbon, boron or similar is applied on the steel surface. In addition to serving as a source for the various diffusion ingredients, the paste protects the steel against contact with the environment, so no packing or gas protection is necessary. Thus, the handling is in general very simple, and the surface strengthening process can be performed in a conventional air furnace. The method provides the same type of surface strengthening that is obtained by more conventional methods. In this work, the main focus will be surface strengthening by carburizing, but also boronizing and boronizing followed by carburizing have been tested out. The methods have been applied to increase the ballistic resistance of the low-strength carbon steel NVE36 (with nominal yield stress of 355 MPa) against impacts from small-arms bullets. An empirical model combining diffusion depth, heat-treatment temperature and soaking time was established on the basis of a series of experimental data. By means of this equation, the various heat-treatment parameters can be predicted when others are chosen. Ballistic perforation tests using 7.62 mm APM2 bullets showed that the low-strength carbon steel after surface strengthening obtained a ballistic limit higher than that of Hardox 400, which is a wear steel with a yield stress of about 1200 MPa.