Sliding friction and wear behaviour of vinylester and its composites under dry and water lubricated sliding conditions

In this paper, we studied and explored the tribological performance of pure vinylester (V), glass fiber reinforced (GFR), SiC filled glass fiber reinforced vinylester composite under dry and water lubricated sliding conditions. Friction and wear tests were carried out with configuration of a pin on a rotating disc under ambient conditions. Tests were conducted at normal load 10, 30 and 50 N and under sliding speed of 1.6 m/s, 2.8 m/s and 4 m/s. The results showed that the coefficient of friction decreases with the increase in applied normal load values both under dry and water lubricated conditions. On the other hand for pure vinylester specific wear rate increases with increase in applied normal load under dry sliding condition and decreases with increase in applied normal load under water lubricated conditions. However the specific wear rate for GFR vinylester composite and SiC filled GFR vinylester composite decreases with the increase in applied normal load both under dry and water lubricated conditions. Moreover, for the range of load and speeds used in this investigation the coefficient of friction and specific wear rates using water lubricant registered lower values than that of the dry condition. The specific wear rates for pure vinylester and vinylester + 50 wt.% GFR and SiC filled GFR vinylester composite under dry and water lubricated sliding condition were in the order of 10−7 mm3 N−1 mm−1.