The effect of production parameters on microstructure and wear resistance of powder metallurgy Al–Al2O3 composite

Aluminum matrix composite is one of the most conventional types of metal matrix composites. This paper deals with the effect of production parameters on wear resistance of Al–Al2O3 composites. Alumina powder with a particle size of 12, 3 and 48 μ and pure aluminum powder with particle size of 30 μ were used. The amount of added alumina powder was up to 20%. Ball milling was utilized to blend the powders. The range of sintering temperature and time were 500, 550 and 600 °C and 30, 45, 60 and 90 min respectively. It was found that increasing sintering temperature results in increasing density, hardness and wear resistance and homogenization of the microstructure. However at certain sintering temperatures and time, considerable grain growth and reduction of hardness value occurred, leading to the degradation of wear resistance. The results showed that at high alumina content, relative density of the composite increases. However, after raising the particle size of alumina, relative density initially increases and then drops to lower values. Increasing weight percent of alumina powder leads to higher hardness and consequently improves the wear resistance of Al–Al2O3 composite. The use of fine alumina particles has a similar effect on hardness and the wear resistance. Finally, a finer grain size was observed, at high amount and low size of the reinforcement particle.