Sliding wear of graphite crystallized chromium white cast iron

The effects of sliding velocity, heat-treatment and graphite shape on sliding wear of graphite crystallized chromium white cast iron were studied. Two types of graphite crystallized chromium white cast irons having flaky or spheroidal and another type of 2.6C–15Cr white cast iron were prepared for this study. The effect of sliding velocity on wear resistance was studied by the Okoshi type and pin-on-disk type wear tests on materials which have experienced “as cast” and “heat-treated” conditions. The Okoshi type wear test results are divided into two relationships depending on sliding velocity or distance. Two regimes, initial wear and steady-state wear, existed for wear loss and sliding distance. A characteristic form of wear curve with a peak and a minimum was obtained when correlating wear loss and sliding velocity. The wear resistance of graphite crystallized chromium white cast irons were superior to that of 2.6C–15Cr white cast iron. In the results of pin-on-disk tests, there was no clear difference in the reported wear loss and friction coefficient among the alloys. However, an opposite tendency has appeared in the wear loss and friction coefficient: the wear loss value reached a peak in the wear curve at 0.52 m/s, while the friction coefficient reached a minimum at 0.52 m/s.