Effect of transfer film structure, composition and bonding on the tribological behavior of polyphenylene sulfide filled with nano particles of TiO2, ZnO, CuO and SiC

The tribological behavior of polyphenylene sulfide (PPS) filled with inorganic nano particles was studied. The fillers investigated were TiO2, ZnO, CuO and SiC whose sizes varied from 30 to 50 nm. The polymer composites were compression molded with varying proportions of these fillers. Wear and friction tests were performed in a pin-on-disk configuration at a sliding speed of 1.0 m/s, nominal pressure of 0.65 MPa, and counterface roughness of 0.10 μm Ra. The polymer composite pins slid against hardened tool steel counterfaces. The transfer films of the composite materials formed on the counterfaces during sliding were studied by optical microscopy and X-ray photoelectron spectroscopy (XPS) and the adhesion between the transfer film and counterface was measured in terms of the peel strength. It was found that the wear rate of PPS decreased when TiO2 and CuO were used as the fillers but increased with ZnO and SiC fillers. The optimum wear resistance was obtained with 2 vol.% CuO or TiO2. These filled composites had the coefficients of friction lower than that of the unfilled PPS. The wear behavior of the composites is explained in terms of the topography of transfer film and adhesion of transfer film to the counterface as observed from peel strength studies. There is a good correlation observed between the transfer film–counterface bond strength and wear resistance.