Tribological performance of α-Fe(Cr)-Fe2B-FeB and α-Fe(Cr)-h-BN coatings obtained by laser melting

α-Fe(Cr)-h-BN and α-Fe(Cr)-Fe2B-FeB coatings on X30Cr13 stainless steel are synthesized by laser melting with incorporation of hexagonal boron nitride, or by alloying of boron. The additive powders are deposited on steel before pulsed irradiation by Nd-YAG laser beam. The solidification structures of the obtained coatings are investigated by optical microscopy and X-ray diffractometry. The mechanical properties are investigated by nanoindentation and the tribological behaviour is characterized on pin-on-disc tribometer, under dry-sliding conditions with different loads and a temperature range 25–500 °C. h-BN-α-Fe(Cr) and Fe2B-α-Fe(Cr) coatings have average hardnesses 10.0 and 14.5 GPa, respectively, while hardness of untreated stainless steel is 4.2 GPa. In comparison with this untreated steel, the sliding contact on ceramic (ruby) of such coating shows a lower coefficient friction and a definitively better wear resistance.