Effective photopolymerization of C60 films under simultaneous deposition and UV light irradiation: Spectroscopy and morphology study Original Research Article

An effective method for uniform photopolymerization of C60 films using simultaneous deposition and irradiation with ultraviolet (UV) light is described. The photopolymerization process was monitored as a function of irradiation time using Raman and infrared (IR) spectroscopy. New features appeared in the Raman (near the pentagonal pinch Ag(2) mode) and IR spectra (400–1500 cm−1) after more than 20 h of UV irradiation testifying to the transformation of pristine C60 to polymerized C60 phases. Band shape analysis of the vibrational data revealed: (i) the degree of photopolymerization to be ∼90% after 20 h of irradiation, and (ii) the presence of orthorhombic, tetragonal, and rhombohedral phases in the photopolymerized films. Electron microscopy and diffraction studies revealed the amorphous nature of the photopolymerized films which comprised of crystals with a linear dimension of ∼40–60 nm. No evidence for cracks in the surface of the polymerized film was found. The proposed route for photopolymerization provides an opportunity to prepare extended polymeric C60 films suitable for technological applications.