Flame synthesis of single-walled carbon nanotubes Original Research Article

Flames offer potential for synthesis of carbon nanotubes in large quantities at significantly lower cost than that of other methods currently available. This study aimed to examine conditions for carbon nanotube formation in premixed flames and to characterize the morphology of solid carbon deposits and their primary formation mechanisms in the combustion environment. Single-walled nanotubes were observed in the post-flame region of a premixed acetylene/oxygen/15 mol% argon flame operated at 6.7 kPa with Fe(CO)5 vapor used as a source of metallic catalyst necessary for nanotube growth. Thermophoretic sampling and transmission electron microscopy were used to characterize the solid material present in the flame at various heights above burner (HAB), providing a quantitative description of formation dynamics within the flame system. Catalyst particle formation and growth is observed to dominate the immediate post-flame region (10–40 mm HAB). Nanotubes were observed to be present after 40 mm HAB with nanotube inception occurring as early as 30 mm HAB. Between 40 and 70 mm HAB, nanotubes were observed to coalesce into clusters. A nanotube formation `windowʹ was evident with formation limited to fuel equivalence ratios between 1.5 and 1.9. A continuum of morphologies ranging from relatively clean clusters of nanotubes to amorphous material was observed between these lower and upper limits. High-resolution transmission electron microscopy and Raman spectroscopy revealed nanotube bundles with each nanotube being single-walled with diameters between 0.9 and 1.5 nm. Particles associated with nanotube bundles were identified as primarily Fe2O3. The estimated yield of nanotubes per unit of material fed to the flame was 0.1 wt% of carbon and 2.5 wt% of iron. A mechanistic interpretation of nanotube formation processes in the premixed flame clearly identifies the role of iron oxide particles and suggests ways for significantly improving the yield of nanotubes from the flame.