Field emission properties of carbon nanotubes synthesized by capillary type atmospheric pressure plasma enhanced chemical vapor deposition at low temperature Original Research Article

Carbon nanotubes (CNTs) were grown using a modified atmospheric pressure plasma with NH3(210 sccm)/N2(100 sccm)/C2H2(150 sccm)/He(8 slm) at low substrate temperatures (⩽500 °C) and their physical and electrical characteristics were investigated as the application to field emission devices. The grown CNTs were multi-wall CNTs (at 450 °C, 15–25 layers of carbon sheets, inner diameter: 10–15 nm, outer diameter: 30–50 nm) and the increase of substrate temperature increased the CNT length and decreased the CNT diameter. The length and diameter of the CNTs grown for 8 min at 500 °C were 8 μm and 40 ± 5 nm, respectively. Also, the defects in the grown CNTs were also decreased with increasing the substrate temperature (The ratio of defect to graphite (ID/IG) measured by FT-Raman at 500 °C was 0.882). The turn-on electric field of the CNTs grown at 450 °C was 2.6 V/μm and the electric field at 1 mA/cm2 was 3.5 V/μm.