A wormhole-structured mesoporous carbon with superior adsorption for dyes Original Research Article

A series of large-pore mesoporous carbon materials with a three-dimensional wormhole framework structure were synthesized by nanocasting using mesoporous silica as a hard template. Samples of hard-template mesoporous silica with pore diameters from 3.08 to 6.43 nm, pore volumes from 0.59 to 1.02 cm3 g−1 and surface areas from 832 to 579 m2 g−1 were prepared from tetraethyl orthosilicate as the silica source and ionic liquid 1-butyl-3-methylimidazolium bromide as structure-directing agent through hydrothermal treatment at different temperatures (110–150 °C) followed by calcining at 550 °C. Subsequently, carbon materials with large pore diameters (2.76–6.70 nm), pore volumes (0.74–2.10 cm3 g−1) and high surface areas (1074–1276 m2 g−1) were synthesized using the various mesoporous silicas synthesized at the different hydrothermal temperatures as a hard-template. The carbon material obtained at a hydrothermal temperature of 150 °C possesses outstanding adsorbility for amaranth and methylene blue dyes.