Microstructural development in equal-channel angular pressing using a 60° die Original Research Article

Billets of pure aluminum and an Al–1%Mg–0.2%Sc alloy were successfully processed using equal-channel angular pressing (ECAP) with a die having an internal channel angle of 60°. Careful inspection of the microstructures after ECAP revealed excellent agreement, at both the macroscopic and the microscopic levels, with the theoretical predictions for shearing using a 60° die. The grain sizes introduced with the 60° die were slightly smaller than with a conventional 90° die; thus, the values with these two dies were ∼1.1 and ∼1.2 μm in pure Al and ∼0.30 and ∼0.36 μm in the Al–Mg–Sc alloy, respectively. Tensile testing of the pure aluminum at room temperature revealed similar strengthening after processing using either a 60° or a 90° die. In tests conducted at 673 K, the Al–Mg–Sc alloy processed with the 60° die exhibited significantly higher elongations to failure due primarily to the larger strain imposed with this die. It is shown using orientation imaging microscopy that superplastic flow in the Al–Mg–Sc alloy produces an essentially random texture and a distribution of boundary misorientations that approximates to the theoretical distribution for an array of randomly oriented grains.