Stability of nanoscale secondary phases in an oxide dispersion strengthened Fe–12Cr alloy Original Research Article

Transmission electron microscopy and atom-probe tomography were used to characterize on a near-atomic scale the microstructure and oxide and carbide phases that form during thermo-mechanical treatments of a model oxide dispersion strengthened Fe–12 wt.% Cr–0.4 wt.% Y2O3 alloy. It was found that some of the Y-rich nanoparticles retained their initial crystallographic structure but developed a Cr-enriched shell, while others evolved into ternary oxide phases during the initial processing. The Y- and Cr-rich oxide phases formed remained stable after annealing at 1023 K for 96 h. However, the number of Cr-rich carbides appeared to increase, inducing Cr depletion in the matrix.