Monosized cationic nanoparticles prepared by emulsifer-free emulsion polymerization

Monosized poly(styrene\N-[3-(dimethylamino)propyl]methacrylamide\poly(ethylene glycol) ethyl ether methacrylate) [poly(St\PEG-EEM\DMAPM)] cationic nanoparticles were synthesized by emulsifier-free emulsion polymerization conducted in the presence of a cationic initiator, 2,2-azobis(2-methylpropionamidine) dihydrochloride (APDH or V-50). Particle sizes and surface charge densities were measured with a Zeta Sizer. The structure of the terpolymers was determined by Fourier transform IR and 1H NMR spectroscopies. The amounts of the main monomer (St), cationic comonomer (DMAPM), stabilizer (PEG-EEM), and initiator (APDH), and the water-to-monomer phase ratio were all effective on both the average size and the surface charge of the nanoparicles. The average particle size was in the range 75–400 nm depending on the recipe applied; it decreased on increasing the amount of DMAP or PEG-EEM or the water-to-monomer phase ratio in the feed, while it increased with increasing St or APDH content. These nanoparticles were quite monodisperse with a polydispersity index of 1.008–1.14.