Residual strength of aluminum–lithium alloy center surface crack tension specimens at cryogenic temperatures Original Research Article

A three parameter fracture criterion which correlates the stress and the stress intensity factor at failure, is followed for the residual or fracture strength estimations of cracked configurations made of aluminum–lithium (Al–Li) alloys. The three fracture parameters are determined from the fracture data of Al–Li alloy center surface crack tension (SCT) specimens at cryogenic temperatures. It is found that the estimated fracture strength values compare well with the test results.