Synthesis of nanocrystalline NiAl by mechanical alloying

The nanocrystalline NiAl intermetallic compound was synthesized by mechanical alloying of the elemental powders. The structural changes of powder particles during mechanical alloying were studied by X-ray diffractometery, scanning electron microscopy and microhardness measurements. The mechanical alloying resulted in the gradual formation of nanocrystalline NiAl with a grain size of 20 nm. It was found that NiAl phase develops by continuous diffusive reaction at Ni/Al layers interfaces. The NiAl compound exhibited high microhardness value of about 1035 Hv.