Interface structure and mechanical properties of Ti(C,N)-based cermet and 17-4PH stainless steel joint brazed with nickel-base filler metal BNi-2

The effects of brazing temperature on microstructure and bonding strength of vacuum brazed joints of Ti(C,N)-based cermet and 17-4 PH stainless steel, using filler metal BNi-2, were investigated. At a lower brazing temperature of 1050 °C, the distribution of melting point depressants (MPD) concentrated on the diffusion affected zone (DAZ) and the brazing seam near the Ti(C,N)-based cermet, the generation of brittle phases in the brazing seam was unavoidable. The uniform distribution of the MPD and full solid solution of γ-nickel occurred in the brazing seam at a higher brazing temperature of 1150 °C. A maximum shear strength of 690 MPa was achieved at a brazing temperature of 1150 °C.