The foundations of a new approach to additive manufacturing: Characteristics of free space metal deposition

In this paper, we report on the realisation of a free space deposition process (FSD). For the first time the use of a moving support structure to deposit tracks of metal starting from a substrate and extending into free space is characterised. The ability to write metal shapes in free space has wide ranging applications in additive manufacturing and rapid prototyping where the tracks can be layered to build overhanging features without the use of fixed support structures (such as is used in selective laser melting (SLM) and stereo lithography (SLA)). We demonstrate and perform a preliminary characterisation of the process in which a soldering iron was used to deposit lead free solder tracks. The factors affecting the stability of tracks and the effect of operating parameters, temperature, velocity, initial track starting diameter and starting volume were measured. A series of 10 tracks at each setting were compared with a control group of tracks; the track width, taper and variation between tracks were compared. Notable results in free space track deposition were that the initial track diameter and volume affected the repeatability and quality of tracks. The standard deviation of mean track width of tracks from the constrained initial diameter group were half that of the unconstrained group. The amount of material fed to the soldering iron before commencing deposition affected the taper of tracks. At an initial volume of 7 mm3 and an initial track diameter of 0.8 mm, none of the ten tracks deposited broke or showed taper > ∼1°. The maximum deposition velocity for free space track deposition using lead-free solder was limited to 1.5 mm s−1.