Gas permeation properties of copolyetherimide based on 1,4-bis(3,4-dicarboxyphenoxy) benzene dianhydride

A series of aromatic homo- and copolyetherimides was prepared from 1,4-bis(3,4-dicarboxyphenoxy) benzene dianhydride with 2,4,6-trimethyl phenylenediamine, 3,3′-dimethyl-4,4′-methylene dianiline, and 3,5-diaminobenzoic acid. The gas permeability coefficients of the copolyetherimides to H2, CO2, O2, N2 and CH4 were measured under 10 atm and at 30°C. A significant change in the permeability and permselectivity resulting from the systematic variation in chemical composition was found. The experimental values of the gas permeability coefficients and permselectivity coefficients of the copolyetherimides are in satisfactory agreement with the values estimated from the gas permeability coefficients of the constituent homopolyimides and their weight fractions.