Effects of annealing on crystallinity and phase behaviour of PET/PC block copolymers

The effects of the annealing on the properties of PET/PC block copolymers, obtained by reactive blending in the presence of different catalysts and for different mixing times, have been studied. The annealing, performed in conditions that promote the crystallization, has been used to better understand the role of block length in determining the phase behaviour. The copolymers characterized by blocks with molecular weight larger than 8000 are able to reorganize towards more ordered domains. This rearrangement maintains the phase separation, as two crystalline phases are present before and after annealing, due to the immiscibility of long blocks. In copolymers characterized by blocks with molecular weight equal to about 2500, that is the higher limit for the miscibility in the amorphous state in PET/PC block copolymers studied in this work, the rearrangement of the chains during annealing causes a phase separation leading to two crystalline phases. Only in the copolymers with molecular weight of blocks lower than 1500, the very short block length hinders the crystallization: therefore, only in this case a phase separation does not take place after annealing.