Rheological and structural properties of aqueous solutions of a hydrophobically modified polyelectrolyte and its unmodified analogue

Rheological methods and small angle neutron scattering (SANS) were used in the characterization of dilute and semidilute aqueous solutions, both with and without added salt, of anionic poly(vinyl alcohol) (PVA−) and its hydrophobically modified analogue (HM-PVA−). The rheological measurements showed that the concentration induced viscosification effect and elastic responses are considerably stronger for solutions of HM-PVA− than in solutions of the unmodified polyelectrolyte. Over the considered polymer concentration domain, the solutions of PVA− exhibit virtually Newtonian behavior, whereas strong shear thinning effects are observed in the HM-PVA− solutions. The SANS results for HM-PVA− solutions reveal a pronounced peak in the plot of scattering intensity versus scattering wavevector q at intermediate q values and the position of the maximum scales with polymer concentration as qmax∼c0.28±0.02. This peak is suppressed in solutions of the unmodified polyelectrolyte and merely a shoulder in the scattering curve appears. Additionally, an “upturn” in the scattered intensity is observed at small q values and the magnitude of this effect depends on polymer concentration, hydrophobicity and salt addition. At large q values, the SANS results from HM-PVA− solutions suggest morphological changes, from rod-like chains to a network of semiflexible chains, as the polyelectrolyte concentration increases.