Copolymerization of ethylene and non-conjugated diene using homogenous catalyst

Ethylene and different amounts of 1,7-octadiene were copolymerized using the metallocene catalyst system ethylidene-bis(fluorenyl) zirconium dichloride and methylaluminoxane (MAO) at both 50 and 90 °C. The catalyst activity has slightly increased with the addition of low amounts of the diene in relation to the homopolymerization of ethylene. The obtained polymers were characterized according to their melting temperature (Tm) and crystallinity degree (xc) by differential scanning calorimetry (DSC). Weight-average molecular weight (Mw) and polydispersity were determined by gel permeation chromatography (GPC). Diene contents in the copolymer were obtained through the FTIR spectroscopy. The results indicated that at polymerization temperature of 90 °C, crosslinking bonds in the obtained copolymers were low, differently from what was observed at 50 °C. The diene content in the copolymer achieved more than 3 mol% and the comonomer conversion was around 15%. Moreover, the obtained copolymers have Mw around 100,000 and large polydispersity.