Direct measurement of gas solubility and diffusivity in poly(vinylidene fluoride) with a high-pressure microbalance

We present solubility and diffusion data for the gases methane and carbon dioxide in the polymer poly(vinylidene fluoride). The polymer was cut from extruded piping intended for use in offshore oil and gas applications. Measurements were carried out using a purpose-built high-pressure microbalance. These properties were determined in the temperature range 80–120 °C and in the pressure range 50–150 bar for methane and 20–40 bar for carbon dioxide. In general, good agreement was obtained for similar measurements reported in the literature. Solubility follows a Henry’s law (linear) dependence with pressure. Diffusion coefficients for each of the gases in the polymer were also measured using the balance. Activation energies for diffusion and heats of solution for the two gases in the polymer were also determined.