A novel type of Si-containing poly(urethane-imide)s: synthesis, characterization and electrical properties

A novel type of a Si-containing poly(urethane-imide) (PUI) was prepared by two different methods. In the first method, Si-containing polyurethane (PU) prepolymer having isocyanate end groups was prepared by the reaction of diphenylsilanediol (DSiD) and toluene diisocyanate (TDI). Subsequently the PU prepolymer was reacted with pyromellitic dianhydride (PMDA) or benzophenonetetracarboxylic dianhydride (BTDA) in N-methyl pyrolidone (NMP) to form Si-containing modified polyimide directly. In the second method, PU prepolymer was reacted with diaminodiphenylether (DDE) or diaminodiphenylsulfone (DDS) in order to prepare an amine telechelic PU prepolymer. Finally, the PU prepolymer having diamine end groups was reacted with PMDA or BTDA to form a Si-containing modified polyimide. Cast films prepared by second method were thermally treated at 160 °C to give a series of clear, transparent PUI films. Thermogravimetric analysis indicated that the thermal degradation of PUI starts at 265 °C which is higher than degradation temperature of conventional PU, confirming that the introduction of imide groups improved the thermal stability of PU. To characterize the modified polyimides and their films, TGA, FTIR, SEM and inherent viscosity analyses were carried out. The dielectrical properties were investigated by the frequency–capacitance method. Dielectric constant, dielectric breakdown strength, moisture uptake and solubility properties of the films were also investigated.