ZnGA–MMT catalyzed the copolymerization of carbon dioxide with propylene oxide

Zinc glutarate (ZnGA) synthesized from zinc oxide and glutarate acid was dispersed on the surface of acid-treated montmorillonite (MMT) in quinoline to prepare ZnGA–MMT catalyst. The results of X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) measurements indicated that the ZnGA on the surface of acid-treated MMT had the same crystalline structure as pure ZnGA. Copolymerization between CO2 and propylene oxide (PO) was carried out under optimized reaction conditions using ZnGA–MMT catalyst, consequently giving poly(propylene carbonate) (PPC) with high molecular weight in a very high yield (115.2 g polymer per gram of ZnGA). The obtained PPCs were investigated using 13C NMR and FTIR spectra, showing a completely alternating structure. Differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) examinations showed the PPCs with a high transition temperature of 38 °C and a very high decomposition temperature (>250 °C) due to the presence of MMT residual in polymer.