Effects of polybutadiene-g-SAN impact modifiers on the morphology and mechanical behaviors of ABS blends

A series of PB-g-SAN impact modifiers with different ratio of PB to SAN ranging from 20.6/79.4 to 91.9/8.1 were synthesized by seeded emulsion polymerization. ABS blends were prepared by blending these PB-g-SAN impact modifiers and SAN resin. The rubber concentration of these ABS blends was kept at a constant value of 15 wt%. The influences of different impact modifier on the mechanical behavior and morphology of ABS blends have been investigated. The dynamic mechanical analysis on ABS blends shows that Tg of the rubbery phase shifts to a lower temperature, (tan δ)max of the rubbery phase increases and then decreases with the increase of PB concentration in PB-g-SAN impact modifier. A uniform dispersion of rubber particles in the matrix can be observed when PB/SAN ratio in PB-g-SAN impact modifier is in the range from 20.6/79.4 to 71.7/28.3. When it exceeds 71.7/28.3, an agglomeration of rubber particles occurs. The mechanical tests indicate that the ABS blend, in which PB/SAN ratio in the impact modifier is 71.7/28.3, has the maximum impact strength and yield strength.