Non-isothermal crystallization kinetics of exfoliated and intercalated polyethylene/montmorillonite nanocomposites prepared by in situ polymerization

Polyethylene/montmorillonite (PE/MMT) nanocomposites, one intercalated sample with higher MMT content and one exfoliated sample with lower MMT content, were prepared by in situ polymerization using MMT-supported metallocene as catalyst. Non-isothermal crystallization behaviors of these two nanocomposites were investigated and compared. The exfoliated sample exhibits higher crystallization temperature (Tc) than the neat PE, showing nucleation effect of MMT. The intercalated sample has lower Tc than the neat PE due to the confinement of MMT. It is observed that the intercalated sample has longer induction period and faster overall crystallization rate, indicating co-existence of suppression and nucleation effects in this sample. The Avrami plots show that the crystal growth of PE in the intercalated sample is two-dimensional, while it is three-dimensional in the exfoliated sample. The crystallization activation energy of the intercalated sample is slightly smaller than that of the exfoliated sample.