Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag — Part II: Effect of Al2O3

The hydration and microstructural evolution of three alkali activated slags (AAS) with Al2O3 contents between 7 and 17% wt.% have been investigated. The slags were hydrated in the presence of two different alkaline activators, NaOH and Na2SiO3·5H2O. The formation of C(single bondA)–S–H and hydrotalcite was observed in all samples by X-ray diffraction, thermal analysis and scanning electron microscopy. Higher Al2O3 content of the slag decreased the Mg/Al ratio of hydrotalcite, increased the Al incorporation in the C(single bondA)-S-H and led to the formation of strätlingite. Increasing Al2O3 content of the slag slowed down the early hydration and a lower compressive strength during the first days was observed. At 28 days and longer, no significant effects of slag Al2O3 content on the degree of hydration, the volume of the hydrates, the coarse porosity or on the compressive strengths were observed.