Characterization, crystallization kinetics and melting behavior of poly(ethylene succinate-co-21 mol% trimethylene succinate) copolyester

A copolyester was synthesized and characterized to have 78.6 mol% ethylene succinate unit and 21.4 mol% trimethylene succinate unit by using NMR. The value of the random parameter is 0.97 that can be considered to be a random copolymer. The melting behavior after isothermal crystallization was studied using differential scanning calorimeter by varying the crystallization temperature, the heating rate and the crystallization time. Triple melting peaks were observed. The melting behavior indicates that the upper melting peaks are primarily due to the melting of lamellar crystals with different stability. The Hoffman–Weeks linear plot gives an equilibrium melting temperature of 94.0 °C. The spherulite growth of this copolyester from 72 °C to 30 or 15 °C at a cooling rate of 1 or 2 °C/min was monitored and recorded using an optical microscope equipped with a CCD camera and a DVD recorder. These experiments including the self-nucleation pretreatment took 72 min and 60 min, respectively. Continuous growth rates between melting and glass transition temperatures can be obtained after curve-fitting procedures. These data fit well with those data points measured in the isothermal experiments, which is time consuming. These isothermal and continuous data were separately analyzed with the Hoffman and Lauritzen theory. A regime II–III transition was detected at about 51.5 ± 0.1 °C.