Effect of nanoscale fully vulcanized acrylic rubber powders on crystallization of poly(butylene terephthalate): Isothermal crystallization

Poly(butylene terephthalate) (PBT) was blended with nanoscale fully vulcanized acrylic rubber (FVAR) powders in a twin extruder, and the FVAR powders were dispersed well in PBT from scanning electron microscopy (SEM) and transmission electron microscope (TEM) investigation. The isothermal crystallization kinetics of PBT/FVAR blends were investigated by differential scanning calorimeter (DSC) and simulated by Avrami model. Equilibrium melting temperature was estimated by the nonlinear Hoffman–Weeks relation. The active energy (ΔE) and nucleation parameters (Kg) increased with the addition of FVAR, suggesting that FVAR particles hindered the crystallization; however more content FVAR had a lower ΔE and Kg because FVAR powders acted as heterogeneous nuclei in the nucleation of crystallization and facilitated the crystallization of PBT. The crystallization ability followed the order: PBT > PBT/FVAR6 > PBT/FVAR3 > PBT/FVAR1 when undercooling was considered.