New hole-transport polyurethanes applied to polymer light-emitting diodes

Polymeric light-emitting diodes (PLEDs) using high-performance hole-transport polyurethanes (PUs) have been fabricated. The PUs were prepared from the condensation polymerization of (E, E)-1,4-bis(2-hydroxystyryl)benzene, an oligo para-phenylene-(E)-vinylene (OPV) unit, with toluene diisocyanate (TDI), isophorone diisocyanate (IPDI) or dicyclohexylmethane 4,4′-diisocyanate (H12MDI), respectively. The condensation polymerization was end-capped with 4-tert-butylphenol as the terminal group. The PLED having the PU layer inserted between PEDOT:PSS (HIL) and MEH-PPV (EML) demonstrated superior current efficiency and low turn-on voltage when comparing to the reference devices of ITO/MEH-PPV(50 nm)/Ca(10 nm)/Ag(100 nm) as well as ITO/PEDOT:PSS(30 nm)/MEH-PPV(50 nm)/Ca(10 nm)/Ag(100 nm). In particularly, the best device performance was realized with the PU of OPV-IPDI as the hole-transport layer, resulting 53 times and 2.72 times of current efficiency enhancement as well as 1.5 V and 1 V voltage reduction of the turn-on voltage, respectively, when compared against the reference devices. Besides, our experiments also showed that the PU polymer could also be applied for flexible PLED with similar performance enhancement. Based on the promising results, we concluded that OPV-IPDI was a good hole-transport material for light-emitting diode application.