Effect of mixed solvent on solution properties and gelation behavior of poly(vinyl alcohol)

In this work, the static and dynamic light scattering measurements were used to investigate the solution properties and the aging effects on PVA/DMSO/water ternary system in dilute region at 25 °C. It was found that the phase separation and aggregate behavior occurs rapidly and obviously when DMSO mole fraction (X1) in the solvent mixture is between 0.2 and 0.33, especially at 0.25. In this solvent composition range, a broad peak which indicates phase separation and chain aggregation can be observed from static light scattering measurement. However, when DMSO mole fraction is increased to 0.37, no such peak is present. For this ternary system, the gelation mechanism and the relationship between the phase separation behavior and the gelation of the formed physical gels were also investigated through the gelation kinetic analyses in the dilute and semi-dilute region. It is concluded that the cononsolvency effect in the dilute solution is not the sole origin that affects the phase separation, aggregation, and gelation behavior for the ternary system in a higher polymer concentration range. The hydrodynamic factors such as the higher viscosity and slower polymer chain diffusion that are resulted from higher polymer concentration should be also considered.