Perfluorinated polymer film with functional group prepared by radiation-induced grafting

A perfluorinated vinyl ether monomer, 2-bromotetrafluoroethyl trifluorovinyl ether (BrTFF) was grafted into crosslinked poly(tetrafluoroethylene) (cPTFE) films by γ-rays irradiation under different conditions. The irradiation with absorbed doses more than 550 kGy gave the poly(BrTFF) grafted cPTFE membranes with grafting yields of more than 20%. FTIR spectra and SEM–EDS testified that BrTFF was successfully grafted into cPTFE films homogeneously in the film perpendicular direction. TGA analysis of the grafted films indicated that the perfluorinated poly(BrTFF) grafts were phase-separated from the PTFE region due to the crosslinked structure of the cPTFE based film, but the grafted films still had high thermal stability (above 300 °C). DSC measurements showed the decrease of melting temperature, but the increase of both heat of fusion and degree of crystallinity in cPTFE film after grafting. The grafted film, a new kind of perfluorinated polymer with bromine active groups and good mechanical properties, is expected to be modified for new applications.