Thermo- and pH-sensitive comb-type grafted poly(N,N-diethylacrylamide-co-acrylic acid) hydrogels with rapid response behaviors

Poly(N,N-diethylacrylamide) with a terminal hydroxyl end group (PDEA-OH) was synthesized by radical telomerization of N,N-diethylacrylamide (DEA) monomer using 2-hydroxyethanethiol as a chain transfer agent. Macromonomer of thermo-sensitive PDEA was synthesized by condensation reaction of PDEA-OH with acryloyl chloride. The macromonomer was characterized by FTIR and 1H NMR, and the molecular weight was determined by GPC. Thermo- and pH-sensitive comb-type grafted poly(N,N-diethylacrylamide-co-acrylic acid) (PDEA-co-AA) hydrogels (GHs) were successfully prepared by grafting PDEA chains with freely mobile ends onto the backbone of a cross-linked (PDEA-co-AA) network. The results showed that the deswelling behavior of the hydrogels was dependent on the test temperature. At 45 °C (beneath the VPTT of the hydrogels), both the normal-type hydrogels (NHs) and comb-type grafted P(DEA-co-AA) hydrogels had lower deswelling rates. While at 60 °C (far beyond the VPTT of the hydrogels), the deswelling rates of the GHs were faster than that of the NHs. Furthermore, pulsatile stimuli-responsive studies indicated that the GHs had excellent thermo-reversibility and were superior to the NHs in the magnitude of their swelling ratios to temperature changes. However, the reversibility to pH changes was poor for both the NHs and the GHs.