N,N′-Diaminoethane linked bis-TEMPO-mediated free radical polymerization of styrene

The N,N′-diaminoethane linked bis-TEMPO nitroxide (C2)-mediated free radical polymerization of styrene at 135 °C in bulk was studied. It was found that under comparable conditions a single nitroxide group of C2 biradical retards the polymerization more than TEMPO. The results were discussed in terms of through-space interactions between two TEMPO moieties of C2 biradical and diffusion effects. According to experimental results analyzed by means of statistical methods, the polymerization system displays a bimodal molecular-weight distribution (MWD) from the beginning of the polymerization process, most probably by undergoing decomposition side reactions leading to irreversible polymer arm (P) separation from PC2P to PC2radical dot and PC2H alkoxyamines. The scale of the decomposition depends rather on the time the system is maintained at the polymerization temperature than on conversion of monomer. Generally, the contribution of low molecular weight chains to overall MWD increases with time of polymerization whereas the contribution of high molecular weight chains to MWD increases for less controlled polymerization systems. For polymers obtained at high [dinitroxide]/[initiator] ratio, the thermal treatment of polystyrene in mass at 135 °C unexpectedly revealed an increase of Mn, which can probably be ascribed to post-polymerization effects involving polystyrene with unsaturated chains end groups.