Synthesis, structures and membrane properties of siloxane-imide co-polymers produced by aqueous polymerization

We report for the first time, the synthesis of siloxane-imide co-polymers by the reaction of mixtures of 1,4-bis(aminobutyl)tetramethyldisiloxane (ABTMDS) and 1,3-bis(4-aminophenoxy)benzene (TPE-R) with bisphenol A diphthalic anhydride (BPADA) using water as the polymerization solvent. A series of co-polymers were prepared incorporating 10, 20, 40 and 100 mol% of ABTMDS with the aromatic diamine TPE-R as the co-monomer. The synthesized co-polymers showed number average molecular weights in the range of 25,000–60,000. As expected the glass transition temperatures (Tgs) and moduli of the polymers were found to decrease with increasing amounts of the siloxane monomer and the homo-polymer containing only the siloxane diamine showing the lowest Tg (60 °C). The resulting polymers could be solution cast into strong and flexible membranes which showed significant decreases in water absorption and moisture permeability compared to the control polymer without siloxane groups. The polymers were characterized by FTIR, 13C and 1H NMR, GPC, DSC and mechanical properties and structural comparisons were made with similar polymers made by standard solvent synthesis methods. Also cross-linked polymers were prepared by the reaction of ABTMDS with the aromatic homo-polymer control and their membrane properties were compared to those of the water synthesized siloxane co-polymers with a similar siloxane content.