Effect of Pd additive on the activity of monolithic LaMnO3-based catalysts for methane combustion

When the perovskites are calcined at 750 °C, the incorporation of Pd into LaMnO3 enhances the activity of the catalyst in methane combustion at temperatures below 750 °C upon substitution of 0.1 mol La with Pd, and at temperatures below 600 °C when Pd is substituted for 0.1–0.15 mol Mn. Monolith catalysts based on La1−xPdxMnO3 (x = 0.1, 0.15) display a higher activity in methane combustion than do LaMn1−xPdxO3-based catalysts, which is due to the higher Pd/(Pd + Mn + La) ratio. The activities of the two perovskite types increase when calcination temperature is raised from 650 to 800 °C. With the increase in calcination temperature, an increase in the Pd content and a decrease in the La content is observed on the surfaces (X-ray photoelectron spectroscopy (XPS)). The rise in the temperature of perovskite calcination to 850 °C produces sintering which leads to the lowering in both the Pd content on the surfaces and the specific surface areas (SSAs) of the perovskites and, consequently, decreases catalytic activity.