Microstructures and Mechanical Properties of Helical Bevel Gears Made by Mn-Cu Alloyed Austempered Ductile Iron Original Research Article

Austempered ductile iron (ADI) has several advantages of replacing cast steel and forged steel in many engineering fields. A new Mn-Cu alloyed ADI with excellent mechanical properties has been developed in order to cut the cost and enlarge the application of ADI. The helical bevel gears were made of the new-developed Mn-Cu alloyed ADI. The microstructure and mechanical properties of the standard sample were investigated by optical microscope (OM), scanning electron microscope (SEM) and performance measurement. The results showed that after a series of treatments, the mechanical properties (Rm 1007.4 to 1200 MPa, A 5.2% to 8.8%, HRC 32 to HRC 35, αK 70 to 120 J/cm2) of the Mn-Cu alloyed ADI standard sample could reach European standard EN1564-97/EN-CJS-1000-5. The surface hardness after helical bevel gears meshing was significantly increased due to the formation of martensite. The bench test and traffic running testing results suggested that the new Mn-Cu alloyed ADI with ultimate life and median life respectively exceeding 30 × 104 and 50 × 104 times could replace 20CrMnTi forged steel for manufacturing the EQ140 helical bevel gears.