Synthesis and characterization of branched yttrium hydroxide fluoride microcrystals with hierarchical tubular structure

Hexagonal yttrium hydroxide fluoride microcrystals were prepared by a two-step hydrothermal route using yttrium nitrate, sodium hydroxide and sodium fluoride as raw materials to react in propanetriol solvent. The samples were characterized by powder X-ray diffraction (XRD), energy dispersive spectrum (EDS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared spectroscopy (FT-IR), thermogravimetre and differential-thermogravimetric analysis (TG-DTA), which revealed that Y(OH)2.14F0.86 microcrystals were multi-branched and that the branches of Y(OH)2.14F0.86 microcrystals were composed of hierarchical tubes. This novel multi-branched and intriguing hierarchical tubular structure of yttrium hydroxide fluoride maybe has a potential application in photoelectric crystals. The formation of branched Y(OH)2.14F0.86 microcrystals with hierarchical tubular structure were due to the substitution reaction and Oswald ripening.